[关键词]
[摘要]
该文以钼酸铵、鸡蛋壳、十六烷基三甲基溴化铵为原材料,通过改变煅烧温度制备了性能更为优良的CaMoO4,并以钼酸钙、硫酸铜、硼氢化钠为原料,制备了CuO/CaMoO4 复合抗菌剂,同时研究了CuO/CaMoO4 复合抗菌剂的用量、培养时间、铜含量对抗菌活性的影响,以及CuO/CaMoO4 复合抗菌剂在光反应和暗反应条件下对大肠杆菌(Escherichia coli,E. coli)的抑菌效果。实验结果表明,在650 ℃煅烧下得到的CuO/CaMoO4 复合抗菌剂的抗菌性能最好,铜含量为1.20% 时,光照条件下和黑暗条件下的抑菌率均能达到100%。含有CuO/CaMoO4 复合抗菌剂的保鲜膜抑菌试验表明,CuO/CaMoO4 复合抗菌剂可以有效抑制食品表面的大肠杆菌,食品经贮藏4 d 后,抑菌率仍为100%。CuO/CaMoO4 复合抗菌剂生物相容性好。CuO/CaMoO4 复合抗菌剂能快速高效抑制大肠杆菌,保障食品安全,为食品贮存行业提供了新的思路。
[Key word]
[Abstract]
In this paper, ammonium molybdate, eggshell and cetyltrimethyl ammonium bromide were used as raw materials to prepare CaMoO4 with improved performance by adjusting the calcination temperature. Additionally, a CuO/CaMoO4 composite antibacterial agent was synthesized using calcium molybdate, copper sulfate, and sodium borohydride as raw materials. The effects of CuO/CaMoO4 antibacterial dosage, culture time, and copper content on antibacterial activity and the antibacterial effect of CuO/CaMoO4 on Escherichia coli (E. coli) were studied under light and dark reaction conditions. The CuO/CaMoO4 composite antibacterial agent synthesized at 650 ℃ exhibited the best antibacterial efficacy. Moreover, when the copper content was 1.20%, the antibacterial rate could reach 100% under light and dark conditions. Bacteriostatic testing of plastic wrapping material containing CuO/CaMoO4 compound antibacterial agent showed that the agent could effectively inhibit E. coli on food surfaces, and the antibacterial rate remained at 100% even after four days of storage. Furthermore, the CuO/CaMoO4 antibacterial compound displayed excellent biocompatibility. Overall, the compound CuO/CaMoO4 antibacterial agent demonstrated rapid and efficient inhibition of E. coli, thereby ensuring food safety and offering novel insights for food storage practices.
[中图分类号]
[基金项目]
中央引导地方科技发展专项(YDZX2021127);山东省高等学校青创人才引育计划-食品加工技术技能创新团队建设项目(2019.133)